RC PEP-Z(HV) Series
Properties
Fast curing. Good adhesion. Water & alcohol resistance.
PREFAC
RC PEP-Z(HV) SERIES is designed for flame-treated PE/PP bottles. High performances and gloss finish can be obtained with reasonable price. PEP-Z(HV) is suitable for high-speed print as it cures with low integral light quantity. All colors are conformed to EN71-3.
APPLICATIONS
Flame-treated polyethylene bottles/polypropyrene bottles.
CHARACTERISTICS
- One-component type. Excellent adhesion.
- PEP-Z(HV) cures with low integral light quantity. Suitable for high-speed print.
- Cured ink film is hard and resistant to scratch.
- Reproducibility of fine patterns is good.
- PEP-Z(HV) do not contain any harmful materials such as heavy metal or N-Vinyl Pyrrolidone. All colors are conformed to EN71-3.
HOW TO USE
- Ink is supplied in ready-to-use condition. Stir well before use.
- Add PEP-Z REDUCER up to 10%, if necessary.
- Add CLEAR to lower density. (Adding ratio is subject to the conditions.)
- PEP-Z(HV) can be usually used without any additive. However, add JAR-18 by 1-3% when the adhesion is not good due to the substrate. The mixture of ink and additive has pot life and should be used up within 12 hours.
- Standard curing conditions: (These conditions change depending on the substrate.)
Metal halide lamp 120W/cm, Distance from focus : 10 cm
Conveyor speed : 20 m/min (Integral light : approx.120 mJ/cm²) - Mesh : Polyester >350 meshes/inch, Thickness of sol : <10 microns
COVERAGE
Approx. 70-90m²/kg
COLOR RANGE
CLEAR, WHITE, OPAQUE WHITE, YELLOW, LEMON YELLOW, ORANGE, BRIGHT RED, RED, GERANIUM, PINK, VIOLET, BLUE, DEEP BLUE, SKY BLUE, MARINE BLUE, GREEN, BLACK
TYPE OF PACKING
1kg PLASTIC CONTAINER
PRECAUTIONS
- The viscosity and printability of the ink change depending on the temperature. The printability in summertime is different from that in wintertime.
- Although skin irritation is low(P.I.I:<2.0), it is advised to avoid skin contact with the ink. In case of contact with skin, wash immediately with soap and water.
- Store the ink in a cool and dark place. Stir occasionally to keep stability when the ink is stored for a long time.
- Stir well before use as de-foamer might be separated.
- You can add JA-950H by 1-2% instead of JAR-18 when better adhesion is required. The cost can be reduced by using JA-950H, although pot life of the mixture is 4-8 hours.
- Please refer to MSDS before use.
- Be sure to do trial print before commercial run to confirm that the product fits the purposes.
PHYSICAL PROPERTIES
- Substrate : HDPE(Wettability is approx.72 dyn/cm by flame treatment.)
- Meshes : Polyester 350 meshes/inch
- Curing : One metal halide lamp 120W/cm, Air-cooling system
- Conveyor speed – 20 m/min. (Integral light : 120 mJ/cm²)
TEST ITEMS | TEST METHODS | RESULTS |
---|---|---|
Adhesion | Cross-hatch, tape-peeling test | 100/100 Pass |
Over-printability | Adhesion test with 3-time-print | Pass |
Alcohol resistance | Peeling test after 24-hour-immersion in 99.5% ethanol. |
100/100 Pass |
Warm water resistance | Peeling test after 24-hour-immersion in warm water of 40°C(104°F). |
100/100 Pass |
- Information given here is gained from our laboratory testing, and no firm guarantee is implied.
- Weathering resistance depends on the color. Please refer to lightfastness chart before use.
Applications Usage
Flame-treated PE/PP bottles.
INK FINDER
Enter a keyword that helps you to find the products which meet your requirements for function, application and substrate.
"Advanced search" makes it possible to find the search conditions from drop-down list.