JUJO TECNICAL INFOMATION

UV-CURE

Oct, 1999

RC PF 42 SERIES

PREFAC

RC PF 42 SERIES forms flexible ink film with matt finish. RC PF is suitable for polycarbonate industrial meters which require post-print processing. RC PF is also recommendable for membrane switches of treated PET films.

APPLICATIONS

Polycarbonate, treated PET films, PVC stickers, rigid vinyl, AS, ABS, acryl(injections), paper

CHARACTERISTICS

  • Flat and matt finish. Excellent flexibility.
  • High density and high opacity.
  • Adhesion and over-printability are good.
  • Reproducibility of fine patterns is good.
  • Stable on the screen.

HOW TO USE

  1. Ink is supplied in ready-to-use condition. Stir well before use. Matt finish can be obtained after UV curing.
  2. Add 42-00 REDUCER up to 10% to lower viscosity. Viscosity is lowered without spoiling matt finish.
  3. The grade of matt finish changes depending on curing conditions or environmental temperature although it does not change after curing. To up-grade matt finish, take more time for levelling.
  4. Standard curing conditions(The conditions depend on the substrates.)
    One metal halide lamp 120 W/cm, Distance from focus : 10 cm
    Conveyor speed : 5 m/min (Integral light : approx. 500 mJ/cm²)
  5. Mesh : 300-350 meshes/inch, Thickness of sol : <10 microns

COVERAGE

70-80 m²/kg

TYPE OF PACKING

1 kg PLASTIC CONTAINER

COLOR RANGE

COLORS

OPAQUE WHITE, LEMON YELLOW, YELLOW, DEEP YELLOW,ORANGE, BRIGHT RED, RED, GERANIUM, VIOLET, DEEP BLUE, BLUE, MARINE BLUE, GREEN, BLACK

CLEAR

    CLEAR, MATT CLEAR, COMPOUND
    HFT MATT CLEAR : Flat and matt
    UB-1 MATT CLEAR : Fine textured surface (high density)
    MATT CLEAR : Fine textured surface (low density)

PRECAUTIONS

  1. Skin irritation(P.I.I.) of each color is low(under 2.0). However, it is advised to avoid skin contact. In case of skin contact, please wash with soap and water immediately.
  2. Store the ink in a cool and dark place. Stir occasionally to keep stability when the ink is stored for a long time.
  3. Stir well before use as de-foamer might be separated.
  4. Standard thickness of colored ink film is 10-12 microns. If the thickness exceeds 15 microns, insufficient curing may cause poor adhesion.
  5. Please refer to MSDS before use.
  6. Be sure to do trial print before commercial run to confirm that the product fits the purposes.

PHYSICAL PROPERTIES

  • Substrate : Polycarbonate (thickness : 0.5 microns) HINTO(TOYOBO), HKU-31(HIGASHIYAMA FILM)
  • Meshes : Polyester 350 meshes/inch, Thickness of sol 10 microns,
  • Thickness of printed ink film : 10 microns
  • Curing : One metal halide lamp 120 W/cm
  • Conveyor speed : 5 m/min. (Integral light : 500 mJ/cm²)
TEST ITEMS TEST METHODS RESULTS
Adhesion Cross-hatch, tape-peeling test 100/100, Pass
Hardness JIS K-5400 8.4 Pencil hardness B-HB
Flexibility Bending test (JIS K-5400 8.1) Excellent
Impact resistance JIS K-5400 8.3 Du Pont Impact tester
1/2 inch, 500 grams, 50 cm
Pass
Over-printability Adhesion test after 3-color-overprint 100/100 Pass
Heat resistance 70°C(158°F), 240 hours Pass
Humidity resistance
60°C(140°F), 95%RH, 240 hours Pass
Coldness resistance -20°C(-4°F), 240 hours Pass
Water-proofness 40°C(104°F)-warm water, 24 hours Pass
Alcohol resistance Rubbing test with 99.5% ethanol Gloss slightly spoiled
after 50 times.
Weathering resistance Sunshine weather meter-400 hours Pass
Key-rubbing resistance Repeated operation with JIS C-5307
based on JIS C-5441
million times : Pass
on treated PET film
188 microns
 1. Weathering resistance depends on the color. Please refer to lightfastness chart before use.
 2. Information given here is gained from our laboratory testing, and no firm guarantee is implied.